Unfolding grain size effects in barium titanate ferroelectric ceramics

Scientific Reports volume 5,

Scientific Reports volume 5, Article number: 9953 (2015) Cite this article

15k Accesses

220 Citations

Metrics details

Grain size effects on the physical properties of polycrystalline ferroelectrics have been extensively studied for decades; however there are still major controversies regarding the dependence of the piezoelectric and ferroelectric properties on the grain size. Dense BaTiO3 ceramics with different grain sizes were fabricated by either conventional sintering or spark plasma sintering using micro- and nano-sized powders. The results show that the grain size effect on the dielectric permittivity is nearly independent of the sintering method and starting powder used. A peak in the permittivity is observed in all the ceramics with a grain size near 1 μm and can be attributed to a maximum domain wall density and mobility. The piezoelectric coefficient d33 and remnant polarization Pr show diverse grain size effects depending on the particle size of the starting powder and sintering temperature. This suggests that besides domain wall density, other factors such as back fields and point defects, which influence the domain wall mobility, could be responsible for the different grain size dependence observed in the dielectric and piezoelectric/ferroelectric properties. In cases where point defects are not the dominant contributor, the piezoelectric constant d33 and the remnant polarization Pr increase with increasing grain size.

Understanding the grain size effects that govern crystal structure and the functional properties of ferroelectrics is of vital importance in improving the performance of ferroelectric systems, which are embedded in a number of electronic devices, such as sensors, actuators, transducers and non-volatile memories1,2,3. Due to a growing demand for miniature devices, significant progress in the fabrication of micro-, meso- and nano-scale ferroelectric structures has been made4,5. A fundamental understanding of grain size effects on the dielectric and ferroelectric properties was achieved by studying low-dimensional ferroelectric structures6,7,8,9,10,11,12. Theoretical and experimental studies on thin/ultrathin films6,7,8, nanowires9,10 and other types of nano-dimensional systems11,12 have shown that ferroelectricity persists down to the nanoscale, thereby demonstrating their potential for use in miniature devices. Nevertheless, certain applications require bulk components with specific functional properties, which can be directly obtained from a specific grain size. Although grain size effects on the dielectric, piezoelectric and ferroelectric properties have been widely studied in several ferroelectric bulk systems, there are still a number of aspects which remain unclear. These are mainly related to the grain size dependency of the piezoelectric and ferroelectric properties, often showing discrepancies in the existing literature. In addition, there are a number of other factors that could influence the grain size dependency; their identification is the main aim of the present study. Barium titanate ceramics are chosen as a model ferroelectric system for this research.

Barium titanate (BaTiO3) is a typical ferroelectric material with a perovskite-type structure. It has been widely studied for dielectric capacitor and lead-free piezoelectric applications, achieving both high dielectric permittivity (up to 7000)13 and piezoelectric constant (d33 up to 788 pC/N in textured ceramics)14 values. In BaTiO3 ceramics, the grain size has been reported to have substantial influence on the dielectric permittivity13,15,16,17,18,19,20,21. The dielectric constant of the BaTiO3 ceramics first increases with decreasing average grain size, reaching a maximum value in the ~ 0.8–1.1 μm grain size range and then rapidly decreases with further decrease of grain size13,15,16,17,18,19,20,21. Similar behaviour has been observed in other ferroelectrics22,23,24. Generally, the grain size dependence of the dielectric permittivity shows consistent trends despite the use of different powder processing and sintering methods13,15,16,17,18,19,20,21. Regarding the physical origin of the maximum value of the permittivity, usually associated with an intermediate grain size of ~ 1 μm, two alternate theories based on internal residual stress and domain wall motion have been developed over the past decades (see Ref. 19 for a review). Recent in situ high energy X-ray diffraction experiments performed on BaTiO3 ceramics with grain sizes in the range 0.32–3.5 µm suggest that the maximum permittivity found around 1 µm grain size is due to maximum domain wall contribution21.

On the other hand, the reported piezoelectric coefficient d33 and its grain size dependence have shown contradicting results in the literature14,21,25,26,27,28,29,30,31,32. For several decades, it has been accepted that the BaTiO3-based ceramics show only modest piezoelectric activity, with a piezoelectric constant d33 lower than 190 pC/N25. Nevertheless, remarkably high d33 values (up to 460 pC/N) have been obtained over recent years for BaTiO3 ceramics (grain size around 1 μm) prepared from hydrothermally synthesized fine powders14,26,27. In addition, a peak of 338 pC/N in the piezoelectric constant was found around the grain size of 1 μm in BaTiO3 ceramics prepared by solid-state reaction and conventional sintering28. Using conventional sintering, it is difficult to obtain dense BaTiO3 ceramics with an average grain size smaller than 1 μm, the relatively low density of these ceramics is considered to have caused the reduction of the piezoelectric constant when compared to the ceramics prepared from hydrothermal powders28. The BaTiO3 ceramics fabricated by the conventional solid state reaction route with a bimodal grain size distribution (large grains had an average size of about 7.0 µm and small grains had an average size of about 0.8 μm) showed a high d33 value of 419 pC/N, which could not be solely attributed to a grain size effect29. Recently, a peak in the d33 was found around 2 µm grain size in barium titanate ceramics and it was concluded that like the permittivity, the maximization of the piezoelectric constant d33 is due to movement of 90° domain walls21. However, for BaTiO3 ceramics prepared from ultrafine powders with grain size ranging from 0.56 to 120 μm, a maximum d33 value was reported at 8.9 μm30, which is larger than the grain size reported in other studies (1–2 μm)21. Additional discrepancies in the grain size dependence of the piezoelectric constant can be found in Refs. 31, 32.

These differences demonstrate that processing conditions can have a significant influence on the physical properties of ferroelectric ceramics. However, at present, the detailed mechanisms for the grain size dependence of the piezoelectric properties in the BaTiO3 ceramics prepared using different processing methods and different starting materials are still unclear.

To solve this controversy, the dependence of the dielectric, piezoelectric and ferroelectric properties on the average grain size of barium titanate ceramics prepared by conventional sintering (CS) and spark plasma sintering (SPS) using micro- and nano-sized powders (see Fig. S1 in supplementary figures) was systematically studied. SPS is an effective way to fabricate dense nanostructured ceramics21,23,33, which could allow for the preparation of a series of fully dense BaTiO3 ceramics with a large range of grain sizes. Through this systematic comparison, the present study highlights the main factors responsible for the controversial grain size dependence previously reported. In addition, it also provides an advanced understanding of the underlying mechanisms of the grain size effect, which will have important implications in maximizing the dielectric, piezoelectric and ferroelectric/ferroelastic properties of other ferroelectric systems.

Table 1 summarizes the room temperature dielectric and piezoelectric properties of poled BaTiO3 ceramics prepared by conventional sintering and SPS from the micro- and nano-sized BaTiO3 powders. In the table, the labels ‘CS’ and ‘SPS’ denote ‘conventional sintering’ and ‘spark plasma sintering’, respectively; the labels ‘micro’ and ‘nano’ describe ceramics sintered using micro- and nano-sized BaTiO3 powder, respectively; while the number after them indicates the sintering temperature. The values of the relative density, average grain size, piezoelectric constant d33, orthorhombic-tetragonal phase transition temperature TO-T and Curie point TC are also listed in the table. The TO-T and TC values were determined from the peaks in the permittivity vs. temperature curves measured during heating. From Table 1 it can be seen that all BaTiO3 samples show high density. For CS-micro BaTiO3 ceramics, the relative density gradually increases from 95.2% to 98.6% and the average grain size increases from 1.3 μm to 32.0 μm with increasing sintering temperature. The relative density of all the SPS samples is larger than 98.5% and the average grain size increases from 0.6 μm to 18.5 μm with increasing sintering temperature.

The room temperature grain size dependence of the permittivity and piezoelectric constant of the poled BaTiO3 ceramics prepared by CS and SPS techniques are plotted using the data in Table 1 and the results are shown in Fig. 1a and Fig. 1b. The dielectric permittivity ε' shows a similar grain size dependence in ceramics sintered by the CS and SPS, as shown in Fig. 1a. The ε' value of the CS-micro ceramics increases from 2730 to 3220 with decreasing grain size (Fig. 1a). Analogously to CS, the permittivity of the SPS ceramics increases with the reduction of grain size and shows a peak around 1 μm. After further reduction of the grain size, the permittivity decreases (Fig. 1a). For SPS-micro BaTiO3 ceramics, the ceramic with an average grain size of 1.2 μm shows the largest permittivity of 4450. The permittivity of the SPS-nano ceramics shows a peak value of 5800 at around 1 μm grain size (Fig. 1a). It can be seen that SPS BaTiO3 ceramics exhibit a larger permittivity than that of the CS-micro ceramics in the whole grain size range. Furthermore, for SPS ceramics, SPS-nano ceramics exhibit a larger permittivity than SPS-micro ceramics in the whole grain size range (Fig. 1a). The grain size dependence of the permittivity observed in this study is in good agreement with the results reported in the literature, although the values show some variations due to the different raw powders and sintering techniques used13,15,16,17,18,19,20,21.

The piezoelectric constant d33 shows the opposite grain size dependence for the two different sintering methods (Fig. 1b). CS-micro BaTiO3 ceramics show a maximum d33 value of 410 pC/N in CS-micro-1230 ceramic with an average grain size of 1.3 μm, which remarkably decreases with increasing grain size (Fig. 1b). The ceramic sintered at 1350°C shows a d33 value of about 180 pC/N (Fig. 1b), which is consistent with the previous results for coarse grained BaTiO3 ceramics25,28. When using the SPS, the piezoelectric constant of the SPS-micro ceramics increases with increasing grain size and shows a maximum value of 430 pC/N in SPS-micro-1200 ceramic with an average grain size of about 4 μm (Fig. 1b). The d33 value decreases with further increase of the sintering temperature above 1200°C (Fig. 1b). Owing to the fine particle size, the sintering temperatures of the SPS-nano ceramics are much lower than those of ceramics prepared from the micro-sized powder. All the SPS BaTiO3 ceramics prepared from the nano-sized powder show a high d33 value (> 300 pC/N). The maximum d33 of SPS-nano BaTiO3 ceramics is close to the maximum d33 of the SPS-micro ceramics. However, the d33 coefficient of the SPS-nano ceramics, unlike that of the SPS-micro ceramics, increases with increasing grain size up to 9.6 μm. By comparing the piezoelectric constant of ceramics sintered by the two different methods, it can be inferred that there is a critical grain size of about 2 μm below which CS-micro BaTiO3 ceramics show a larger d33. The maximum d33 for both the BaTiO3 ceramics sintered by the CS and SPS show a remarkably large value of over 400 pC/N.

Figure 2 shows the polarization-electric field (P-E) hysteresis loops of the unpoled BaTiO3 ceramics sintered by the CS and SPS. All of the ceramics except CS-micro-1350 show slim P-E hysteresis loops with a coercive field (Ec) lower than 0.35 kV/mm, which is close to the value reported by other researchers25,31. The grain size dependence of the maximum polarization (Pmax) and remnant polarization (Pr) of the CS and SPS BaTiO3 ceramics is shown in Fig. 3. It can be seen that for CS ceramics, both Pmax and Pr decrease with increasing grain size (Figs. 3a, 3b). The CS-micro samples show a larger Pr than the SPS ceramics when the grain size is below 2 μm and a lower value when the grain size is above 2 μm (Fig. 3b). In the SPS-micro ceramics the maximum polarization Pmax slightly increases with increasing grain size and the values are larger than those of the CS-micro samples. The remnant polarization Pr slightly increases and gradually saturates for grain sizes larger than 2 µm; meanwhile it dramatically decreases when the grain size is below 2 μm. For the SPS-nano ceramics, the Pmax slightly increases with increasing grain size and Pr dramatically increases for grain sizes larger than 4.5 µm (Fig. 3b), which is consistent with the grain size dependence of d33 shown in Fig. 1. Figure 3c shows that the CS-micro-1350 sample (32 µm average grain size) exhibits a coercive field of 0.35 kV/mm which is larger than that of the CS-micro-1230 (1.3 µm average grain size; Ec = 0.17 kV/mm) and CS-micro-1280 ceramics (5.8 µm average grain size; Ec = 0.175 kV/mm). For the SPS-micro ceramics, Ec gradually decreases from 0.3 kV/mm to 0.17 kV/mm with increasing grain size. A similar grain size dependence of the coercive field is shown by the SPS-nano ceramics (Fig. 3c).

Grain size dependence of (a) maximum polarization Pmax, (b) remnant polarization Pr and (c) coercive field EC for BaTiO3 ceramics prepared by different sintering methods from micro- and nano-sized powders.

Figure 4 shows SEM images of the domain patterns of several poled BaTiO3 ceramics prepared from micro- and nano-sized powders. The microstructures of the CS-micro ceramics are displayed in Figs. 4a and 4b. Figs. 4c to 4f show images of the SPS-micro ceramics, while Figs. 4g and 4h show the domain structures of two typical SPS-nano ceramics. For fine-grained BaTiO3 ceramics, the domain patterns mainly consist of stripes marked as ‘S’ running across the whole grain, as visible in Figs. 4a and 4c. The stripe lengths increase and the average domain width becomes larger as the grain size increases. The stripes are believed to correspond to 90° domain patterns34,35. The formation of 90° domains is a consequence of the relief of internal stresses in the BaTiO3 ceramics when cooled from a high temperature to below TC34,35. Herringbone patterns marked as ‘H’ consisting of two adjacent sets of parallel stripes were occasionally found, especially in coarse grained samples with grain sizes larger than 2 μm, as shown in Figs. 4b, 4e, 4f and 4h. These have been reported as typical domain structures of tetragonal BaTiO3 ceramics34,35,36,37,38. In addition, a small amount of watermarks labelled as ‘W’ (believed to correspond to 180°-domain boundaries)28,34, were often observed in coarse grained BaTiO3 ceramics and rarely appear in fine grains (Figs. 4b, 4f and 4h). This suggests the existence of 180° domains in coarse grained BaTiO3 ceramics after poling, indicating that either it was not possible to align all the 180° domains during poling or that the ceramics lost part of the domain alignment on removal of the field after the poling process.

Domain structures of BaTiO3 ceramics.

(a) CS-micro-1230; (b) CS-micro-1350; (c) SPS-micro-1080; (d) SPS-micro-1120; (e) SPS-micro-1200; (f) SPS-micro-1240; (g) SPS-nano-1040; (h) SPS-nano-1160. ‘S’ denotes stripe domain structure, ‘H’ denotes herringbone domain structure and ‘W’ denotes watermark domain structure.

The domain width of the striped domain structure was measured at a large number of locations in ceramics with different grain size and an average was calculated. The resultant grain size dependence of the average domain width for BaTiO3 ceramics prepared by different sintering methods is shown in Fig. 5. It can be seen that the average domain width decreases with decreasing grain size for all BaTiO3 ceramics. From Fig. 5 it is clear that there is a deviation from the parabolic relationship between domain width and grain size previously reported in ferroelectric ceramics36,39. Deviations from the parabolic law were also found in other ferroelectric systems and have been recently discussed in the literature40,41. When the grain size is larger than 4 μm, the CS ceramics and SPS ceramics show a similar grain size dependence of the domain width. The value of the domain width of the fine-grained BaTiO3 ceramics is consistent with that typically reported in literature (~ 100 nm)17,28,29,31. The average domain width of the coarse-grained ceramics is much smaller than the previously reported values (larger than 500 nm)17,34.

Grain size dependence of the average domain width for the CS and SPS BaTiO3 ceramics.

It is well known that the dielectric and piezoelectric properties of ferroelectric ceramics include intrinsic and extrinsic contributions; the former originates from the deformation of the unit cell under an external electric or mechanical field, while the latter is mainly due to domain wall movement and point defects42,43,44,45,46,47,48. The domain wall contribution is determined by the domain wall density and domain wall mobility, which are also both influenced by many factors including grain size, back fields and defects42,43,44,45,46,47,48. The differences in the grain size dependence of the piezoelectric properties of the CS and SPS BaTiO3 ceramics can be interpreted based on the following aspects.

The average domain width decreases with the reduction of the average grain size in BaTiO3 ceramics sintered by both methods, as demonstrated in Fig. 5, which is in agreement with Refs. 38, 40. This means that the number of domain walls per volume (the domain wall density) increases with decreasing grain size. This could contribute to a maximum in domain wall activity, which would produce an enhancement of the dielectric and piezoelectric properties in correspondence with a specific grain size. Optimum domain wall density could be one possible reason for the maximum permittivity observed near 1 µm grain size in CS and SPS ceramics (see Fig. 1a), as also suggested in previous reports13,15,16,17,18,19,21. However, domain wall density is not the only factor which controls the domain wall contribution in ferroelectric/ferroelastic materials and additional factors should be taken into account in unravelling all the grain size effects observed.

Back fields are a result of restoring forces acting on domain walls during domain switching49. The back fields may oppose the switching during electric field loading and assist the back-switching during electric field unloading. A larger grain boundary area in fine grained ceramics would produce a back field which would exert a clamping effect on domain walls making the ferroelectric/ferroelastic domains harder to switch during the application of an electric field50,51. This explains why the Ec value of the SPS ceramics decreases with increasing grain size (Fig. 3c). In the case of the SPS-nano ceramics, the piezoelectric constant and the remnant polarization both decrease with decreasing average grain size in the entire range studied (Figs. 1b, 3b). The decrease of Pr with decreasing grain size can be attributed to an increased effect of the back field in ceramics with smaller grains. Back fields can also induce a reduction of the d33 in accordance with the following scenarios, which may also overlap: a) the increased back field in ceramics with smaller grains might hinder domain alignments during DC poling; b) the back field reduces the alignment of the domains when the electric field is removed after the DC poling process.

In order to achieve high density in conventional sintering, the sintering temperatures are higher and the dwelling times are much longer than those utilized in the SPS method. It was suggested that this represents a possible cause of point defects in the ceramics prepared by the conventional route52. Point defects tend to migrate to the domain boundaries or grain boundaries and subsequently pin the domain walls53,54,55,56,57. In our BaTiO3 samples, domain wall pinning effects seem to increase with increasing sintering temperature as demonstrated in Fig. 3 by the increase of Ec and the decrease of Pmax with increasing grain size in CS-micro ceramics. Figure 6 shows the temperature dependence of the dielectric permittivity of the BaTiO3 ceramics prepared from different powders using different sintering methods. The peaks near 120°C correspond to the Curie point Tc of BaTiO3. The broad peaks in the dielectric permittivity at high temperature from 400 to 700°C, often observed in perovskite-type ferroelectric oxides including BaTiO3, can be attributed to the motion of oxygen vacancies as suggested by the calculated activation energy reported in Ref. 58. The peak intensity increases with increasing sintering temperature for CS-micro ceramics (Figs. 6a and b). In addition, the X-ray Photoelectron Spectroscopy (XPS) analysis shows that the valence state of barium and oxygen changes with increasing sintering temperature, reflecting possible modifications in the Ba-O coordination and stoichiometry, which could be accommodated by the formation of oxygen vacancies (refer to supporting Figure S2). In Figs. 6c and d, the intensity of the high temperature dielectric peaks decreases with reduction of the sintering temperature for SPS-micro ceramics. Further evidence for the presence of point defects (i.e. oxygen vacancies) in SPS-micro ceramics sintered at high temperatures are represented by the existence of an additional current peak that appears in the current-electric field (I-E) curves at temperatures starting from 80°C (refer to supporting Figures S3a and S3b), an additional loss peak at a low frequency of about 100 Hz (refer to supporting Figures S3c and S3d) and by an asymmetric strain-electric field loop (refer to supporting Figures S3e and S3f). The high temperature broad peaks in the dielectric permittivity are almost absent in SPS-nano ceramics (Fig. 6e) due to the lower sintering temperature used.

The presence of point defects can reduce the domain wall mobility, thereby decreasing the extrinsic contribution of domain walls to the dielectric and piezoelectric properties. Domain wall pinning by point defects can have an important contribution to the reduction of the dielectric permittivity with increasing grain size in CS ceramics and for the lower permittivity of CS samples compared to SPS ceramics (Fig. 1a). For piezoelectric properties, the existence of point defects restricts domain switching under the DC poling process resulting in a poor domain alignment after poling, which leads to a lower piezoelectric constant. In addition, the small oscillating force used to measure the piezoelectric constant may not be large enough to counteract the pinning effect caused by the point defects resulting in the decrease of d33 with increasing grain size in the CS-micro ceramics. In CS-micro ceramics, the remnant polarization and the piezoelectric constant both decrease with increasing grain size over the entire range studied. This suggests that the effect of domain wall pinning increases with increasing sintering temperature, resulting in a larger coercive field and a significant decrease of Pmax in CS-micro ceramics with the largest grain size (see Figs. 1b and 3a–3c). In Fig. 2, the coarse grained SPS ceramics exhibit more saturated P-E hysteresis loops and much larger Pr values than those of the CS-micro ceramics. In addition, the maximum polarization Pmax of SPS ceramics increases with increasing grain size in the range studied (Fig. 3a). The effects of sintering temperature on domain wall activity is also evidenced by the different grain size dependence of the piezoelectric constant observed for the SPS-micro ceramics and SPS-nano ceramics (Fig. 1). The latter were sintered at much lower temperatures and show a constant increase in the d33 over the same grain size range. These observations indicate that when the sintering temperature becomes too high, the effect of domain wall pinning by point defects becomes the main factor in determining the observed grain size dependence of the piezoelectric and ferroelectric properties.

In order to clarify the different grain size dependencies of the permittivity and piezoelectric constant, the SPS-nano ceramics will be considered first as the contribution of point defects to the grain size dependence observed is presumably not dominant and the grain size dependence of the permittivity and d33 shows the most remarkable differences among the ceramics studied here (Figs. 1a, 1b). Considering the P-E loop (Fig. 2c) and the S-P loop (Fig. S4c) of the SPS-nano-1160, it can be inferred that in the region around the coercive field the domain switching process is dominated by 180° domain reorientation. This is evidenced by the steep change in polarization and the minor strain change in the region around the coercive field (P = 0), as shown in the hysteresis plots of Fig. 2c and Fig. S4c. In addition, the SEM images of the domain structure suggest an increased presence of 180° domains in SPS-nano-1160 compared to the other SPS-nano ceramics. Therefore, it is unlikely that the permittivity of SPS-nano-1160 is mainly dominated by the 180° domain wall contribution; otherwise it would not be the lowest among all the SPS-nano ceramics (Fig. 1a). On the other hand, the d33 of SPS-nano-1160 is the largest within the SPS-nano ceramics, due to the smaller back field experienced by this ceramic, which allowed for a higher degree of domain alignment during DC poling and a limited back-switching after poling. This is in agreement with the largest value of Pr in SPS-nano-1160, among all the SPS-nano ceramics studied. Since it was deduced that the contribution of 180° domain walls to the permittivity is not dominant, it can be inferred that the back field acts on 90° domains. By definition, the dielectric permittivity indicates the amount of polarization change that can be induced under the application of an electric field, thus it should be expected that the permittivity generally decreases with increasing domain alignment after DC poling, as confirmed by previous experiments28. Therefore the smallest permittivity in the SPS-nano-1160 with the largest grain size among the poled SPS-nano ceramics should be attributed to a smaller contribution of 90° domain walls due to a limited back-switching of 90° domains after poling, in comparison to the other SPS-nano ceramics (see also Supporting Information S4). The dominant contribution of 90° domain walls to the dielectric permittivity has been unambiguously proven in PbZr0.2Ti0.8O3 thin films59. With decreasing grain size, the d33 decreases because of the increase of the back field according to the scenarios a) and b) previously described, while the permittivity increases, because of a larger contribution of 90° domain walls. When the grain size becomes too small, the contribution of 90° domain walls decreases and the permittivity of the poled ceramics starts to decrease with decreasing grain size (below 1 µm in BaTiO3 ceramics). Similar arguments apply to the permittivity of the SPS-micro ceramics and the CS-micro ceramics, for which the grain size dependence of the d33 has already been explained.

In the attempt to understand the grain size dependence observed in barium titanate ferroelectric ceramics, highly convoluted effects were observed on dielectric, piezoelectric and ferroelectric properties, which can be summarized as follows. The grain size dependence of the dielectric permittivity is mostly independent of both the starting powders and sintering process used. The maximum dielectric permittivity at a critical grain size of about 1 µm is mainly achieved by optimum density and mobility of 90° domain walls.

The grain size dependence of the piezoelectric constant is instead affected by additional factors related to ceramic processing, including particle size of the starting powder and sintering temperature. With increasing grain size, the d33 of CS-micro ceramics decreases over the whole grain size range; the d33 of SPS-micro ceramics first increases and then decreases with a peak at 4.3 μm grain size; the d33 of SPS-nano ceramics increases over the entire grain size range studied. The increase of d33 in the SPS-nano ceramics and in the SPS-micro ceramics below 4.3 μm is due to an increased domain alignment caused by a reduction of the back field exerted by grain boundaries with increasing grain size. Domain wall pinning by point defects is instead the main factor for the decrease of the d33 in SPS-micro ceramics above 4.3 μm and in CS-micro ceramics over the entire grain size range.

Regarding the ferroelectric properties, it was observed that the coercive field of SPS ceramics decreases with increasing grain size, while in CS ceramics it increases in ceramics with larger grains. The latter is attributed to an increased pinning effect on domain walls by point defects developed in ceramics sintered at high temperature. In ceramics where the point defects contribution is not dominant, the maximum and remnant polarization increase with increasing grain size.

Grain size effects on dielectric, piezoelectric and ferroelectric properties of three different groups of BaTiO3 ceramics with distinct sintering temperature ranges were studied. This allowed for a wider view of the possible grain size dependencies which could be observed in ferroelectric ceramics. Grain size effect is influenced by contributions from ferroelectric domain walls, back fields and point defects developed during sintering at high temperatures. The maximum dielectric permittivity near 1 µm grain size is achieved by optimum density and mobility of 90° domain walls in all the BaTiO3 ceramics studied. In ceramics sintered by SPS at low temperatures (T < 1200°C), the grain size dependence of the piezoelectric and ferroelectric properties can be mainly attributed to the degree of domain alignment and the influence of the back field exerted by the grain boundaries. In ceramics sintered at high temperatures either by SPS or CS, there is an additional contribution from point defects, which increases with increasing sintering temperature and influences the domain wall contribution to the grain size effect observed. When studying grain size effects in ferroelectric materials, the point defects contribution should be minimized to avoid contradicting and misleading observations.

Conventional micro-sized BaTiO3 powders were prepared from commercial BaCO3 (purity ≥ 99.0%) and TiO2 (purity ≥ 99.8%) powders. The BaCO3 and TiO2 powders were weighed according to the stoichiometric formula and ball-milled for 12 h in nylon pots with ZrO2 balls and alcohol as a milling media. The slurry was then dried and ground using an agate mortar and pestle. The powder mixture was calcined at 1050°C for 4 h. After the second ball-milling, a fine BaTiO3 powder with average particle size lower than 0.5 μm was obtained. Hydrothermal synthesized nano-powders of BaTiO3 with a particle size of 100 nm were also used as the precursor materials. The microstructures of different BaTiO3 powders are shown in Fig. S1.

Two kinds of sintering techniques were adopted to sinter BaTiO3 ceramics: conventional sintering (CS) and Spark Plasma Sintering (SPS). In the case of CS, the micro-sized BaTiO3 powders (Fig. S1a) were pressed into pellets of 15 mm diameter and 1 mm thickness and then sintered at 1210°C, 1280°C and 1350°C for 2 h in air (referred as CS-micro-1210, CS-micro-1280 and CS-micro-1350 for abbreviation). In the case of the SPS samples, BaTiO3 micro-sized powders were sintered in vacuum for 5 minutes under an uniaxial pressure of 85 MPa at 1080°C, 1100°C, 1120°C, 1200°C and 1240°C (referred as SPS-micro-1080, SPS-micro-1100, SPS-micro-1120, SPS-micro-1200 and SPS-micro-1240 for abbreviation) using a SPS furnace (HPD-25/1 FCT systeme GmbH). The 100 nm nanopowder (Fig. S1b) was sintered by the SPS unit at 1000°C, 1020°C, 1040°C, 1060°C and 1160°C (referred as SPS-nano-1000, SPS-nano-1020, SPS-nano-1040, SPS-nano-1060 and SPS-nano-1160 for abbreviation). All the SPS samples were annealed in air at 900°C for 2 h to eliminate the presence of any residual carbon and reduction effects incurred during SPS process.

The density of the ceramics was measured by the Archimedes method. For electrical characterization, disk-shaped specimens were coated with a silver paint (Gwent Electronic Materials Ltd, C2011004D5, Pontypool, UK) on the top and bottom surfaces and fired at 600°C for 20 min. Poling was carried out at 105°C in silicon oil under an electric field of 3.0 kV/mm for 30 min. The piezoelectric d33 coefficient was measured using a Berlincourt-type d33 meter (model YE 2730A, Sinocera Piezotronics, China). The dielectric properties were measured using an impedance analyzer (Agilent 4294A). The polarization hysteresis (P-E) loops were traced using a ferroelectric hysteresis measurement tester (NPL, Teddingdon, UK)60,61. For the microstructure and domain configuration characterization, the poled specimens were mirror-polished and chemically etched for 10 s in an aqueous solution of 5% HCl with a small amount of HF (3 drops of HF:20 ml HCl solution). The microstructure and domain structure observations were performed using a scanning electron microscope (SEM; model JEOL JSM 6300). X-ray photoelectron spectroscopy (XPS; ESCALAB MK II, VG Scientific) was carried out to study the valence state of ions in the ceramics sintered at different temperatures.

Haertling, G. H. Ferroelectric ceramics: history and technology. J. Am. Ceram. Soc. 82, 797–818 (1999).

Article CAS Google Scholar

Scott, J. F. Applications of modern ferroelectrics. Science 315, 954–957 (2007).

Article CAS ADS Google Scholar

Yang, L. F. et al. Bipolar loop-like non-volatile strain in the (001)-oriented Pb(Mg1/3Nb2/3)O3-PbTiO3 single crystals. Sci. Rep. 4, 4591 (2014).

Article Google Scholar

Dawber, M. K., Rabe, M. & Scott, J. F. Physics of thin-film ferroelectric oxides. Rev. Mod. Phys. 77, 1083–1130 (2005).

Article CAS ADS Google Scholar

Gruverman, A. & Kholkin, A. Nanoscale ferroelectrics: processing, characterization and future trends. Rep. Prog. Phys. 69, 2443–2474 (2006).

Article CAS ADS Google Scholar

Shaw, T. M., Trolier-McKinstry, S. & McIntyre, P. C. The Properties of ferroelectric films at small dimensions. Annu. Rev. Mater. Sci. 30, 263–298 (2000).

Article CAS ADS Google Scholar

Fong, D. D. et al. Ferroelectricity in ultrathin perovskite films. Science 304, 1650–1653 (2004).

Article CAS ADS Google Scholar

Spaldin, N. A. Fundamental size limits in ferroelectricity. Science 304, 1606–1607 (2004).

Article CAS Google Scholar

Spanier, J. E. et al. Ferroelectric phase transition in individual single-crystalline BaTiO3 nanowires. Nano Lett. 6, 735–739 (2006).

Article CAS ADS Google Scholar

Yun, W. S., Urban, J. J., Gu, Q. & Park, H. K. Ferroelectric properties of individual barium titanate nanowires investigated by scanned probe microscopy. Nano Lett. 2, 447–450 (2002).

Article CAS ADS Google Scholar

Polking, M. J. et al. Ferroelectric order in individual nanometre-scale crystals. Nat. Mater. 11, 700–709 (2012).

Article CAS ADS Google Scholar

Wu, C. M. et al. Controllability of vortex domain structure in ferroelectric nanodot: fruitful domain patterns and transformation paths. Sci. Rep. 4, 3946 (2014).

Article CAS Google Scholar

Hoshina, T. et al. Domain size effect on dielectric properties of barium titanate ceramics. Jpn. J. Appl. Phys. 47, 7607–7611 (2008).

Article CAS ADS Google Scholar

Wada, S. et al. Preparation of [110] grain oriented barium titanate ceramics by templated grain growth method and their piezoelectric properties. Jpn. J. Appl. Phys. 46, 7039–7043 (2007).

Article CAS ADS Google Scholar

Kniepkamp, H. & Heywang, W. Z. Depolarisationseffekte in polykristallin gesinterem BaTiO3. Angew. Phys.6, 385 (1954).

Kinoshita, K. & Yamaji, A. Grain-size effects on dielectric properties in barium titanate ceramics. J. Appl. Phys. 47, 371–373 (1976).

Article CAS ADS Google Scholar

Arlt, G., Hennings, D. & De With, G. Dielectric properties of fine-grained barium-titanate ceramics. J. Appl. Phys. 58, 1619–1625 (1985).

Article CAS ADS Google Scholar

Bell, A. J., Moulson, A. J. & Cross, L. E. The effect of grain size on the permittivity of BaTiO3 . Ferroelectrics 54, 147–150 (1984).

Article Google Scholar

Bell, A. J. Grain size effects in barium titanate – revisited. Paper presented at Applications of Ferroelectrics, Proceedings of the Ninth IEEE International Symposium, University Park, PA. IEEE. (DOI:10.1109/ISAF.1994.522286) (7 Aug 1991).

Buessem, W. R., Cross, L. E. & Goswami, A. K. Phenomenological theory of high permittivity in fine-grained barium titanate. J. Am. Ceram. Soc. 49, 33–36 (1966).

Article CAS Google Scholar

Ghosh, D. et al. Domain wall displacement is the origin of superior permittivity and piezoelectricity in BaTiO3 at intermediate grain sizes. Adv. Func. Mater. 24, 885–896 (2014).

Article CAS Google Scholar

Randall, C. A., Kim, N., Kucera, J., Cao, W. W. & Shrout, T. R. Intrinsic and extrinsic size effects in fine-grained morphotropic-phase-boundary lead zirconate titanate ceramics. J. Am. Ceram. Soc. 81, 677–688 (1988).

Article Google Scholar

Zhang, H. T. et al. The grain size effect on the properties of Aurivillius phase Bi3.15Nd0.85Ti3O12 ferroelectric ceramics. Nanotechnology 20, 385708 (2009).

Article Google Scholar

Huo, S. X., Yuan, S. L., Tian, Z. M., Wang, C. H. & Qiu, Y. Grain size effects on the ferroelectric and piezoelectric properties of Na0.5K0.5NbO3 ceramics prepared by pechini method. J. Am. Ceram. Soc. 95, 1383–1387 (2012).

Article CAS Google Scholar

Jaffe, B., Cook, W. R. & Jaffe, H. Piezoelectric Ceramics. London: Academic, UK, 1971.

Takahashi, H. et al. Lead-free barium titanate ceramics with large piezoelectric constant fabricated by microwave sintering. Jpn. J. Appl. Phys. 45, L30–L32 (2006).

Article CAS Google Scholar

Karaki, T., Yan, K. & Adachi, M. Barium titanate piezoelectric ceramics manufactured by two-step sintering. Jpn. J. Appl. Phys., 46, 7035–7038 (2007).

Article CAS ADS Google Scholar

Zheng, P., Zhang, J. L., Tan, Y. Q. & Wang, C. L. Grain-size effects on dielectric and piezoelectric properties of poled BaTiO3 ceramics. Acta Mater. 60, 5022–5030 (2012).

Article CAS Google Scholar

Shao, S. F. et al. High piezoelectric properties and domain configuration in BaTiO3 ceramics obtained through solid-state reaction route. J. Physics D: Appl. Phys., 41, 125408 (2008).

Article ADS Google Scholar

Ding, S. H., Song, T. X., Yang, X. J. & Luo, G. H. Effect of grain size of BaTiO3 ceramics on dielectric properties. Ferroelectrics 402, 55–59 (2010).

Article CAS Google Scholar

Huan, Y., Wang, X. H., Fang, J. & Li, L. T. Grain size effects on piezoelectric properties and domain structure of BaTiO3 ceramics prepared by two-step sintering. J. Am. Ceram. Soc. 96, 3369–3371 (2013).

Article CAS Google Scholar

Egerton, L. & Koonce, S. E. Effect of firing cycle on structure and some dielectric and piezoelectric properties of barium titanate ceramic. J. Am. Ceram. Soc. 38, 412–418 (1955).

Article CAS Google Scholar

Viola, G. et al. Effect of grain size on domain structures, dielectric and thermal depoling of Nd-substituted bismuth titanate ceramics. Appl. Phys. Lett. 103, 182903 (2013).

Article ADS Google Scholar

Arlt, G. & Sasko, P. Domain configuration and equilibrium size of domains in BaTiO3 ceramics. J. Appl. Phys. 51, 4956–4960 (1980).

Article CAS ADS Google Scholar

Arlt, G. Twinning in ferroelectric and ferroelastic ceramics: stress relief. J. Mater. Sci. 25, 2655–2666 (1990).

Article CAS ADS Google Scholar

Baxter, P., Hellicar, N. J. & Lewis, B. Effect of additives of limited solid solubility on ferroelectric properties of barium titanate ceramics. J. Am. Ceram. Soc. 42, 465–470 (1956).

Article Google Scholar

Devries, R. C. & Burke, J. E. Microstructure of barium titanate ceramics. J. Am. Ceram. Soc. 40, 200–206 (1957).

Article CAS Google Scholar

Chou, J. F., Lin, M. H. & Lu, H. Y. Ferroelectric domains in pressureless-sintered barium titanate. Acta Mater. 48, 3569–3579 (2000).

Article CAS Google Scholar

Cao, W. W. & Randall, C. A. Grain size and domain size relations in bulk ceramic ferroelectric materials. J. Phys. Chem. Solids 57, 1499–1505 (1996).

Article CAS ADS Google Scholar

Eriksson, M. et al. Ferroelectric domain structures and electrical properties of fine-grained lead-free sodium potassium niobate ceramics. J. Am. Ceram. Soc. 94, 3391–3396 (2011).

Article CAS Google Scholar

Scott, J. F. Cylinder stress in nanostructures: effect on domains in nanowires, nanotubes and nano-disks. J. Phys.: Condens. Matter 26, 212202 (2014).

CAS ADS Google Scholar

Li, S. P., Cao, W. W. & Cross, L. E. The extrinsic nature of nonlinear behavior observed in lead zirconate titanate ferroelectric ceramic. J. Appl. Phys. 69, 7219–7224 (1991).

Article CAS ADS Google Scholar

Zhang, Q. M., Wang, H., Kim, N. & Cross, L. E. Direct evaluation of domain-wall and intrinsic contributions to the dielectric and piezoelectric response and their temperature dependence on lead zirconate-titanate ceramics. J. Appl. Phys. 75, 454 (1991).

Article ADS Google Scholar

Demartin, M. & Damjanovic, D. Dependence of the direct piezoelectric effect in coarse and fine grain barium titanate ceramics on dynamic and static pressure. Appl. Phys. Lett. 68, 3046–3048 (1996).

Article CAS ADS Google Scholar

Damjanovic, D. Stress and frequency dependence of the direct piezoelectric effect in ferroelectric ceramics. J. Appl. Phys. 82, 1788–1797 (1997).

Article CAS ADS Google Scholar

Damjanovic, D. Contributions to the piezoelectric effect in ferroelectric single crystals and ceramics. J. Am. Ceram. Soc. 88, 2663–2676 (2005).

Article CAS Google Scholar

Arlt, G. & Pertsev, N. A. Force constant and effective mass of 90° domain walls in ferroelectric ceramics. J. Appl. Phys. 70, 2283–2289 (1991).

Article ADS Google Scholar

Luchaninov, A. G., Shil'nikov, A. V., Shuvalov, L. A. and Shipkova, I. Ju. The domain processes and piezoeffect in polycrystalline ferroelectrics. Ferroelectrics 98, 123–126 (1989).

Article CAS Google Scholar

Viola, G., Chong, K. B., Guiu, F. & Reece, M. J. Role of internal field and exhaustion in ferroelectric switching. J. Appl. Phys. 115, 034106 (2014).

Article ADS Google Scholar

Cao, W. Ferroelectrics: The strain limits on switching. Nat. Mater. 4, 727–728 (2005).

Article CAS ADS Google Scholar

Martirena, H. T. & Burfoot, J. C. Grain-size effects on properties of some ferroelectric ceramics. J. Phys. C: Solid State Phys. 7, 3182–3192 (1974).

Article CAS ADS Google Scholar

Waser, R. Solubility of hydrogen defects in doped and undoped BaTiO3 . J. Am. Ceram. Soc. 71, 58–63 (1988).

Article CAS Google Scholar

Yoo, I. K. & Desu, S. B. Fatigue parameters of lead zirconate titanate thin films. Mater. Res. Soc. Symp. Proc. 243, 323 (1992).

Article CAS Google Scholar

Scott, J. F. & Paz de Arajuo, C. A. Ferroelectric memories. Science 246, 1400–1405 (1989).

Article CAS ADS Google Scholar

He, L. & Vanderbilt, D. First-principles study of oxygen-vacancy pinning of domain walls in PbTiO3 . Phys. Rev. B 68, 134103 (2003).

Article ADS Google Scholar

Choi, Y., Hoshina, T., Takeda, H. & Tsurumi, T. Effect of oxygen vacancy and oxygen vacancy migration on dielectric response of BaTiO3-Based Ceramics. Jpn. J. Appl. Phys. 50, 031504 (2011).

Article ADS Google Scholar

Oyama, T., Wada, N. & Takagi, H. Trapping of oxygen vacancy at grain boundary and its correlation with local atomic configuration and resultant excess energy in barium titanate: a systematic computational analysis. Phys. Rev. B 82, 134107 (2010).

Article ADS Google Scholar

Kang, B. S., Choi, S. K. & Park, C. H. Diffuse dielectric anomaly in perovskite-type ferroelectric oxides in the temperature range of 400–700°C. J. Appl. Phys. 94, 1904–1911 (2003).

Article CAS ADS Google Scholar

Karthik, J., Damodaran, A. R. & Martin, L. W. Effect of 90° domain walls on the low-field permittivity of PbZr0.2Ti0.8O3 thin films. Phys. Rev. Lett. 108, 167601 (2012).

Article CAS ADS Google Scholar

Yan, H. X. et al. The contribution of electrical conductivity, dielectric permittivity and domain switching in ferroelectric hysteresis loops. J. Adv. Dielectr. 1, 107–118 (2011).

Article CAS Google Scholar

Viola, G. et al. Contribution of piezoelectric effect, electrostriction and ferroelectric/ferroelastic switching to strain-electric field response of dielectrics. J. Adv. Dielectr. 3, 1350007 (2013).

Article ADS Google Scholar

Download references

This work was financially supported by the Specialized Research Fund for the Doctoral Program of Higher Education (Grant No. 20130131110006) and the National Natural Science Foundation of China (Grant No. 51172128). The authors thank Prof. D. R. Chen of Shandong University for providing the hydrothermally-synthesized fine BaTiO3 powder. We would also like to thank China Scholarship Council for the financial support of 1 years research in the UK. One of the authors, V. Koval, acknowledges the support of the Grant Agency of Slovak Academy of Sciences through Grant No. 2/0057/14.

School of physics, State Key Laboratory of Crystal Materials, Shandong University, Jinan, 250100, P.R. China

Yongqiang Tan, Jialiang Zhang, Yanqing Wu & Chunlei Wang

Institute of Materials Research, Slovak Academy of Sciences, Watsonova 47, 040 01, Kosice, Slovakia

Vladimir Koval

School of Engineering and Applied Science, Aston University, Birmingham, B4 7ET, United Kingdom

Baogui Shi & Haitao Ye

School of Engineering and Materials Science, Queen Mary University of London, Mile End Road, London, E1 4NS, United Kingdom

Yongqiang Tan, Ruth McKinnon, Giuseppe Viola & Haixue Yan

Department of Applied Science and Technology, Institute of Materials Physics and Engineering, Corso Duca degli Abruzzi 24, Torino, 10129, Italy

Giuseppe Viola

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

T.Y.Q., Z.J.L., K.V., W.C.L., R.M., V.G. and Y.H.X. wrote the main manuscript text, W.Y.Q. prepared Figure 1, T.Y.Q. prepared Figures 2–6 and Figures S1, 3, S.B.G. and Y.H.T prepared Figures S2. All authors reviewed the manuscript.

Grain size dependence of (a) the dielectric permittivity and (b) the piezoelectric d33 constant of the poled BaTiO3 ceramics prepared by the conventional and SPS techniques from micro- and nano-sized powders.

The conventional sintering temperatures are 1230°C, 1280°C and 1350°C; the SPS sintering temperatures for the micro-sized powder are 1080°C, 1100°C, 1120°C, 1200°C and 1240°C and for the nano-sized powder are 1000°C, 1020°C, 1040°C, 1060°C and 1160°C.

P-E loops of BaTiO3 ceramics prepared from different powders and sintered at different temperatures.

(a) CS-micro ceramics; (b) SPS-micro ceramics; (c) SPS-nano ceramics.

Temperature dependence of dielectric permittivity for BaTiO3 ceramics.

(a), (b) CS-micro ceramics; (c), (d) SPS-micro ceramics; (e), (f) SPS-nano ceramics.

The authors declare no competing financial interests.

Unfolding grain size effects in Barium Titanate ferroelectric ceramics

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

Tan, Y., Zhang, J., Wu, Y. et al. Unfolding grain size effects in barium titanate ferroelectric ceramics. Sci Rep 5, 9953 (2015). https://doi.org/10.1038/srep09953

Download citation

Received: 29 October 2014

Accepted: 24 March 2015

Published: 07 May 2015

DOI: https://doi.org/10.1038/srep09953

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Journal of Materials Science: Materials in Electronics (2023)

Journal of Materials Science: Materials in Electronics (2022)

Journal of Electroceramics (2022)

Journal of Materials Science: Materials in Electronics (2022)

Journal of Materials Science: Materials in Electronics (2021)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.